Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of Badalac® ABS/PA 320 GF30 UV - (ABS+PA*)-GF30 - Bada AG

Material Data Center offers the following functions for Badalac® ABS/PA 320 GF30 UV:
unit conversion, PDF datasheet print, comparison with other plastics, snap fit calculation, beam deflection calculation, CAE Interfaces

Check here, which other Badalac datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Processing/Physical Characteristics - Mechanical properties - Thermal properties - Electrical properties - Other properties - Processing Recommendation Injection Molding
Any use of this information falls under the rules of our disclaimer.
Processing/Physical CharacteristicsValueUnitTest Standard
ISO Data
Melt volume-flow rate, MVR 60 cm³/10min ISO 1133
Temperature 240 °C -
Load 10 kg -
Mechanical propertiesValueUnitTest Standard
ISO Data
Tensile Modulus 8100 MPa ISO 527
Stress at break 130 MPa ISO 527
Strain at break 3 % ISO 527
Flexural strength 180 MPa ISO 178
Charpy impact strength, +23°C 50 kJ/m² ISO 179/1eU
Charpy impact strength, -30°C 35 kJ/m² ISO 179/1eU
Charpy notched impact strength, +23°C 9 kJ/m² ISO 179/1eA
Charpy notched impact strength, -30°C 6 kJ/m² ISO 179/1eA
Thermal propertiesValueUnitTest Standard
ISO Data
Temp. of deflection under load, 1.80 MPa 185 °C ISO 75-1/-2
Temp. of deflection under load, 0.45 MPa 175 °C ISO 75-1/-2
Vicat softening temperature, A 125 °C ISO 306
Burning behav. at 1.5 mm nom. thickn. HB class IEC 60695-11-10
Thickness tested 1.5 mm -
Burning behav. at thickness h HB class IEC 60695-11-10
Thickness tested 0.8 mm -
Electrical propertiesValueUnitTest Standard
ISO Data
Volume resistivity 1E11 Ohm*m IEC 62631-3-1
Surface resistivity 1E12 Ohm IEC 62631-3-2
Comparative tracking index 600 - IEC 60112
Other propertiesValueUnitTest Standard
Water absorption 4.5 % Sim. to ISO 62
Humidity absorption 1.5 % Sim. to ISO 62
Density 1280 kg/m³ ISO 1183
Processing Recommendation Injection MoldingValueUnitTest Standard
Pre-drying - Temperature 80 °C -
Pre-drying - Time 2 - 4 h -
Processing humidity ≤0.1 % -
Melt temperature 240 - 260 °C -
Mold temperature 70 - 90 °C -
Characteristics
Processing
Injection Molding
Special Characteristics
U.V. stabilized or stable to weather
Regional Availability
North America, Europe, Asia Pacific, South and Central America, Near East/Africa
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com