Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of KOPA® KN133G15BR - PA6-GF15 - Kolon Industries

Material Data Center offers the following functions for KOPA® KN133G15BR:
unit conversion, PDF datasheet print, comparison with other plastics

Check here, which other Kopa datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Processing/Physical Characteristics - Mechanical properties - Thermal properties - Electrical properties - Other properties - Processing Recommendation Injection Molding
Any use of this information falls under the rules of our disclaimer.
Processing/Physical CharacteristicsValueUnitTest Standard
ISO Data
Molding shrinkage, parallel 0.5 % ISO 294-4, 2577
Molding shrinkage, normal 0.6 % ISO 294-4, 2577
ASTM Data
Mold Shrinkage, MD 0.009 mm/mm ASTM D 955
Mechanical propertiesValueUnitTest Standard
ISO Data
Tensile Strength 130 MPa ISO 527
Flexural modulus, 23°C 5200 MPa ISO 178
Charpy notched impact strength, +23°C 8 kJ/m² ISO 179/1eA
Rockwell hardness R 118 - ISO 2039-2
ASTM Data
Tensile Strength 123 MPa ASTM D 638
Flexural Modulus 5541 MPa ASTM D 790
Flexural Strength 196 MPa ASTM D 790
Rockwell Hardness R 120 - ASTM D 785
Izod Impact notched, 1/8 in 108 J/m ASTM D 256
Thermal propertiesValueUnitTest Standard
ISO Data
Melting temperature, 10°C/min 225 °C ISO 11357-1/-3
Temp. of deflection under load, 1.80 MPa 185 °C ISO 75-1/-2
ASTM Data
UL 94 Flame rating HB - UL 94
Thickness tested 0.8 mm -
Coefficient of Thermal Expansion, MD 40 E-6/K ASTM D 696
DTUL @ 66 psi 205 °C ASTM D 648
DTUL @ 264 psi 190 °C ASTM D 648
Melting Temperature 220 °C ASTM D 3418
Electrical propertiesValueUnitTest Standard
ASTM Data
Dielectric Strength, Short Time 21 kV/mm ASTM D 149
Dielectric Constant, 1 MHz 3.6 - ASTM D 150
Arc Resistance 130 s ASTM D 495
Other propertiesValueUnitTest Standard
Density 1240 kg/m³ ISO 1183
Water Absorption, 24hr 0.4 % ASTM D 570
Density 1250 kg/m³ ASTM D 792
Processing Recommendation Injection MoldingValueUnitTest Standard
Pre-drying - Temperature 80 - 100 °C -
Pre-drying - Time 4 - 5 h -
Processing humidity ≤0.05 % -
Mold temperature 60 - 80 °C -
Zone 1 230 °C -
Zone 2 240 °C -
Zone 3 245 °C -
Nozzle temperature 250 °C -
Characteristics
Processing
Injection Molding
Special Characteristics
Heat stabilized or stable to heat
Regional Availability
North America, Asia Pacific
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com