Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of MAGNUM™ 3325 MT - ABS - Trinseo

Material Data Center offers the following functions for MAGNUM™ 3325 MT:
unit conversion, PDF datasheet print, comparison with other plastics, snap fit calculation, beam deflection calculation, CAE Interfaces

Check here, which other Magnum datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Processing/Physical Characteristics - Mechanical properties - Thermal properties - Other properties
Any use of this information falls under the rules of our disclaimer.
Processing/Physical CharacteristicsValueUnitTest Standard
ISO Data
Melt volume-flow rate, MVR 11 cm³/10min ISO 1133
Temperature 220 °C -
Load 10 kg -
Melt flow index, MFI 10 g/10min ISO 1133
Temperature 220 °C -
Load 10 kg -
Molding shrinkage, parallel 0.6 % ISO 294-4, 2577
ASTM Data
Melt Flow Index, MFI 2.5 g/10min ASTM D 1238
Temperature 230 °C -
Load 3.8 kg -
Mold Shrinkage, MD 0.0055 mm/mm ASTM D 955
Mechanical propertiesValueUnitTest Standard
ISO Data
Tensile Modulus 2200 MPa ISO 527
Yield stress 43 MPa ISO 527
Yield strain 3.3 % ISO 527
Flexural modulus, 23°C 2100 MPa ISO 178
Charpy notched impact strength, +23°C 17 kJ/m² ISO 179/1eA
Charpy notched impact strength, -30°C 11 kJ/m² ISO 179/1eA
Izod notched impact strength, +23°C 17 kJ/m² ISO 180/1A
Izod notched impact strength 10 kJ/m² ISO 180/1A
Temperature -30 °C -
ASTM Data
Tensile Modulus 2068 MPa ASTM D 638
Tensile Strength at Yield 42.3 MPa ASTM D 638
Elongation at Break 25 % ASTM D 638
Flexural Modulus 2206 MPa ASTM D 790
Flexural Strength 64.5 MPa ASTM D 790
Izod Impact notched, 1/8 in 310 J/m ASTM D 256
Thermal propertiesValueUnitTest Standard
ISO Data
Vicat softening temperature, B 102 °C ISO 306
Burning behav. at 1.5 mm nom. thickn. HB class IEC 60695-11-10
Thickness tested 1.5 mm -
Burning behav. at thickness h HB class IEC 60695-11-10
Thickness tested 3.0 mm -
ASTM Data
UL 94 Flame rating HB - UL 94
Thickness tested 1.5 mm -
Coefficient of Thermal Expansion, MD 93.6 E-6/K ASTM D 696
DTUL @ 66 psi 96.1 °C ASTM D 648
DTUL @ 264 psi 82.8 °C ASTM D 648
Vicat Temperature 108 °C ASTM D 1525
Other propertiesValueUnitTest Standard
Density 1050 kg/m³ ISO 1183
Density 1040 kg/m³ ASTM D 792
Characteristics
Features
Color Stability
Applications
Automotive
Regional Availability
North America, Asia Pacific, South and Central America
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com