Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of NOPLA® KE101 - (PEN+PET) - Kolon Industries

Material Data Center offers the following functions for NOPLA® KE101:
unit conversion, PDF datasheet print, comparison with other plastics

Check here, which other Nopla datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Processing/Physical Characteristics - Mechanical properties - Thermal properties - Optical properties - Other properties - Processing Recommendation Injection Molding
Any use of this information falls under the rules of our disclaimer.
Processing/Physical CharacteristicsValueUnitTest Standard
ISO Data
Melt flow index, MFI 15 g/10min ISO 1133
Temperature 275 °C -
Load 2.16 kg -
Molding shrinkage, parallel 0.6 % ISO 294-4, 2577
ASTM Data
Melt Flow Index, MFI 8.1 g/10min ASTM D 1238
Temperature 260 °C -
Load 1.05 kg -
Mold Shrinkage, MD 0.005 mm/mm ASTM D 955
Mechanical propertiesValueUnitTest Standard
ISO Data
Tensile Strength 60 MPa ISO 527
Flexural modulus, 23°C 2900 MPa ISO 178
Charpy notched impact strength, +23°C 3.5 kJ/m² ISO 179/1eA
Rockwell hardness R 88 - ISO 2039-2
ASTM Data
Tensile Strength 60 MPa ASTM D 638
Flexural Modulus 2854 MPa ASTM D 790
Flexural Strength 92 MPa ASTM D 790
Rockwell Hardness R 88 - ASTM D 785
Thermal propertiesValueUnitTest Standard
ISO Data
Melting temperature, 10°C/min 230 °C ISO 11357-1/-3
Temp. of deflection under load, 0.45 MPa 75 °C ISO 75-1/-2
Burning behav. at thickness h V-2 class IEC 60695-11-10
Thickness tested 0.8 mm -
ASTM Data
UL 94 Flame rating V-2 - UL 94
Thickness tested 0.8 mm -
Coefficient of Thermal Expansion, MD 60 E-6/K ASTM D 696
DTUL @ 66 psi 77 °C ASTM D 648
Melting Temperature 234 °C ASTM D 3418
Optical propertiesValueUnitTest Standard
ASTM Data
Haze 1 % ASTM D 1003
Light Transmittance 85 % ASTM D 1003
Other propertiesValueUnitTest Standard
Density 1330 kg/m³ ISO 1183
Density 1330 kg/m³ ASTM D 792
Processing Recommendation Injection MoldingValueUnitTest Standard
Pre-drying - Temperature 140 - 160 °C -
Pre-drying - Time 3 - 6 h -
Processing humidity ≤0.08 % -
Mold temperature 30 - 80 °C -
Zone 1 160 - 210 °C -
Zone 2 200 - 240 °C -
Zone 3 220 - 250 °C -
Nozzle temperature 230 - 265 °C -
Characteristics
Processing
Injection Molding
Special Characteristics
Transparent
Features
Copolymer
Regional Availability
North America, Asia Pacific
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com