| Processing/Physical Characteristics | dry / cond | Unit | Test Standard |
| ISO Data |
| Melt volume-flow rate, MVR |
14 / * |
cm³/10min |
ISO 1133 |
| Temperature |
275 / * |
°C |
- |
| Load |
5 / * |
kg |
- |
| Molding shrinkage, parallel |
1.0 / * |
% |
ISO 294-4, 2577 |
| Molding shrinkage, normal |
0.9 / * |
% |
ISO 294-4, 2577 |
| Mechanical properties | dry / cond | Unit | Test Standard |
| ISO Data |
| Tensile Modulus |
3900 / 1600 |
MPa |
ISO 527 |
| Tensile Strength |
90 / 45 |
MPa |
ISO 527 |
| Yield strain |
4 / 25 |
% |
ISO 527 |
| Strain at break |
7 / >50 |
% |
ISO 527 |
| Flexural modulus, 23°C |
3500 / 1300 |
MPa |
ISO 178 |
| Flexural strength |
116 / 50 |
MPa |
ISO 178 |
| Charpy impact strength, +23°C |
70 / - |
kJ/m² |
ISO 179/1eU |
| Charpy impact strength, -30°C |
60 / - |
kJ/m² |
ISO 179/1eU |
| Charpy notched impact strength, +23°C |
5 / 20 |
kJ/m² |
ISO 179/1eA |
| Thermal properties | dry / cond | Unit | Test Standard |
| ISO Data |
| Melting temperature, 10°C/min |
222 / * |
°C |
ISO 11357-1/-3 |
| Temp. of deflection under load, 1.80 MPa |
80 / * |
°C |
ISO 75-1/-2 |
| Temp. of deflection under load, 0.45 MPa |
200 / * |
°C |
ISO 75-1/-2 |
| Coeff. of linear therm. expansion, parallel |
90 / * |
E-6/K |
ISO 11359-1/-2 |
| Coeff. of linear therm. expansion, normal |
90 / * |
E-6/K |
ISO 11359-1/-2 |
| Burning behav. at 1.5 mm nom. thickn. |
V-0 / * |
class |
IEC 60695-11-10 |
| Thickness tested |
1.5 / * |
mm |
- |
| Glow Wire Flammability Index (GWFI) |
960 |
°C |
IEC 60695-2-12 |
| GWFI - thickness tested (1) |
1.5 |
mm |
- |
| Glow Wire Ignition Temperature (GWIT) |
775 |
°C |
IEC 60695-2-13 |
| GWIT - thickness tested (1) |
1.5 |
mm |
- |
| Electrical properties | dry / cond | Unit | Test Standard |
| ISO Data |
| Comparative tracking index |
600 / - |
- |
IEC 60112 |
| Other Standards[S] |
| Relative permittivity, 1MHz |
3.5 / 7 |
- |
IEC 60250 |
| Dissipation factor, 1MHz |
300 / 3000 |
E-4 |
IEC 60250 |
| Volume resistivity |
1E13 / 1E10 |
Ohm*m |
IEC 60093 |
| Surface resistivity |
* / 1E10 |
Ohm |
IEC 60093 |
| S: | These properties are reported by the producer according standards that are different to our defaults. |
| Other properties | dry / cond | Unit | Test Standard |
| Water absorption |
9 / * |
% |
Sim. to ISO 62 |
| Humidity absorption |
2.5 / * |
% |
Sim. to ISO 62 |
| Density |
1180 / - |
kg/m³ |
ISO 1183 |
| Material specific properties | dry / cond | Unit | Test Standard |
| ISO Data |
| Viscosity number |
263 / * |
cm³/g |
ISO 307, 1157, 1628 |
| Processing Recommendation Injection Molding | Value | Unit | Test Standard |
| Pre-drying - Temperature |
<80 |
°C |
- |
| Pre-drying - Time |
4 - 6 |
h |
- |
| Melt temperature |
260 - 280 |
°C |
- |
| Mold temperature |
40 - 80 |
°C |
- |
| Processing Recommendation Extrusion | Value | Unit | Test Standard |
| Pre-drying - Temperature |
80 |
°C |
- |
| Pre-drying - Time |
4 - 6 |
h |
- |
| Melt temperature |
230 - 280 |
°C |
- |
Characteristics
Processing
Injection Molding, Other Extrusion
Additives
Lubricants
Special Characteristics
Flame retardant, Halogen-free, Heat stabilized or stable to heat
Regional Availability
Europe
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.