Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of CELANEX® 2000FC - PBT - Celanese

Material Data Center offers the following functions for CELANEX® 2000FC:
unit conversion, PDF datasheet print, comparison with other plastics, snap fit calculation, beam deflection calculation, CAE Interfaces

Check here, which other Celanex datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Caratteristiche Fisiche - Proprietà Meccaniche - Proprietà Termiche - Proprietà Elettriche - Altre Proprietà - Raccomandazione de Processabilità Stampaggio ad Iniezione
Any use of this information falls under the rules of our disclaimer.
Caratteristiche FisicheValoreUnitáNorma del test
ISO Data
Indice di fusione di volume, MVR 65 cm³/10min ISO 1133
Temperatura 250 °C -
Carico 2.16 kg -
Proprietà MeccanicheValoreUnitáNorma del test
ISO Data
Modulo a trazione 2700 MPa ISO 527
Carico unitario a trazione 60 MPa ISO 527
Deformazione a snervamento 4 % ISO 527
Deformazione nominale a rottura 30 % ISO 527
Resistenza all'urto Charpy, +23°C 100 kJ/m² ISO 179/1eU
Resistenza all'urto Charpy, -30°C 90 kJ/m² ISO 179/1eU
Resistenzia all'urto Charpy con intaglio, +23°C 4 kJ/m² ISO 179/1eA
Resistenzia all'urto Charpy con intaglio, -30°C 3.5 kJ/m² ISO 179/1eA
Proprietà TermicheValoreUnitáNorma del test
ISO Data
Temperatura di fusione, 10°C/min 225 °C ISO 11357-1/-3
Temperatura di transizione vetrosa, 10°C/min 60 °C ISO 11357-1/-2
Temp.di inflessione sotto carico, 1.80 MPa 55 °C ISO 75-1/-2
Temp.di inflessione sotto carico, 0.45 MPa 155 °C ISO 75-1/-2
Temp.di rammollimento Vicat, B 190 °C ISO 306
Coeff.di dilatazione termica lin., parallelo 110 E-6/K ISO 11359-1/-2
Coeff.di dilatazione termica lin., perpend. 86 E-6/K ISO 11359-1/-2
Indice di ossigeno 22 % ISO 4589-1/-2
Proprietà ElettricheValoreUnitáNorma del test
ISO Data
Costante dielettrica relativa, 100Hz 4 - IEC 62631-2-1
Costante dielettrica relativa, 1MHz 3.5 - IEC 62631-2-1
Fattore di dissipazione, 100Hz 15 E-4 IEC 62631-2-1
Fattore di dissipazione, 1MHz 200 E-4 IEC 62631-2-1
Resistività volumica >1E13 Ohm*m IEC 62631-3-1
Resistività superficiale >1E15 Ohm IEC 62631-3-2
Rigidità dielettrica 23 kV/mm IEC 60243-1
Altre ProprietàValoreUnitáNorma del test
Assorbimento d'acqua 0.45 % Sim. alla ISO 62
Assorbimento d'umidità 0.25 % Sim. alla ISO 62
Massa volumica 1310 kg/m³ ISO 1183
Raccomandazione de Processabilità Stampaggio ad IniezioneValoreUnitáNorma del test
Pre-essiccamento - Temperatura 121 °C -
Pre-essiccamento - Tempo 4 h -
Umidità del Processo ≤0.02 % -
Temperatura di fusione 235 - 260 °C -
Temperatura dello stampo 65 - 93 °C -
Caratteristiche
Processabilità e Forma di Forni
Stampaggio ad Iniezione, Altre Estrusioni
Forma fisica disponibile
Pellet
Certifications
Contatto con gli alimenti
Disponibilità geografica
Nord America, Europa, Asia Oceano Pacifico
Altre informazioni
Stampaggio ad Iniezione
To avoid hydrolytic degradation during processing, CELANEX resins have to be dried to a moisture level equal to or less than 0.02%. Drying should be done in a dehumidifying hopper dryer capable of dewpoints <-30°F (-34°C) at 250°F (121°C) for 4 hours.
Rear Temperature 450-470(230-240) deg F (deg C)
Center Temperature 460-480(235-250) deg F (deg C)
Front Temperature 470-500(240-260) deg F (deg C)
Nozzle Temperature 480-500(250-260) deg F (deg C)
Melt Temperature 460-500(235-260) deg F (deg C)
Mold Temperature 150-200(65-93) deg F (deg C)
Back Pressure 0-50 psi
Screw Speed Medium
Injection Speed Fast

Injection speed, injection pressure and holding pressure have to be optimized to the individual article geometry. To avoid material degradation during processing low back pressure and minimum screw speed have to be used. Overheating of the material has to be avoided, in particular for flame retardant grades. Up to 25% clean and dry regrind may be used.
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com