Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of MAGNUM™ 3325 SLG - ABS - Trinseo

Material Data Center offers the following functions for MAGNUM™ 3325 SLG:
unit conversion, PDF datasheet print, comparison with other plastics, snap fit calculation, beam deflection calculation, CAE Interfaces

Check here, which other Magnum datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Processing/Physical Characteristics - 機械的特性 - 熱的特性 - その他の特性. - Processing Recommendation Injection Molding
Any use of this information falls under the rules of our disclaimer.
Processing/Physical Characteristics値単位テスト基準
ISO データ
メルトフローレート, MFI 3.1 g/10min ISO 1133
温度 230 °C -
荷重 3.8 kg -
成形収縮率, 平行 0.5 % ISO 294-4, 2577
成形収縮率, 直角 0.5 % ISO 294-4, 2577
ASTM数据
メルトフローレイト, MFI 3.1 g/10min ASTM D 1238
温度 230 °C -
荷重 3.8 kg -
機械的特性値単位テスト基準
ISO データ
引張弾性率 1920 MPa ISO 527
降伏応力 37 MPa ISO 527
降伏ひずみ 2.8 % ISO 527
破壊ひずみ 19 % ISO 527
曲げ弾性率, 23°C 2070 MPa ISO 178
ノッチ付きシャルピー衝撃強さ, +23°C 16 kJ/m² ISO 179/1eA
ノッチ付きシャルピー衝撃強さ, -30ﾟC 11 kJ/m² ISO 179/1eA
ノッチ付きIzod衝撃強さ, +23°C 18 kJ/m² ISO 180/1A
ノッチ付きIzod衝撃強さ 11 kJ/m² ISO 180/1A
温度 -30 °C -
ASTM数据
引張弾性率 2075 MPa ASTM D 638
降伏応力 40 MPa ASTM D 638
降伏点伸び 2.8 % ASTM D 638
破断伸び 22 % ASTM D 638
曲げ弾性率 2144 MPa ASTM D 790
曲げ強さ 64.1 MPa ASTM D 790
ノッチ付きIzod衝撃強さ, 1/8 in 187 J/m ASTM D 256
ノッチ付きIzod衝撃強さ, Low-Temperature 128 J/m ASTM D 256
温度 -30 °C -
熱的特性値単位テスト基準
ISO データ
荷重たわみ温度, 1.80 MPa 82 °C ISO 75-1/-2
荷重たわみ温度, 0.45 MPa 97 °C ISO 75-1/-2
ビカット軟化温度, B 101 °C ISO 306
ASTM数据
線膨張係数, 平行 82.8 E-6/K ASTM D 696
線膨張係数, 直角 90 E-6/K ASTM D 696
DTUL @ 66 psi 96.7 °C ASTM D 648
DTUL @ 264 psi 82.2 °C ASTM D 648
ビカット軟化温度 101 °C ASTM D 1525
その他の特性.値単位テスト基準
密度. 1050 kg/m³ ISO 1183
密度 1050 kg/m³ ASTM D 792
Processing Recommendation Injection Molding値単位テスト基準
Pre-drying - Temperature 82 - 85 °C -
Pre-drying - Time ≥2 h -
樹脂温度 243 - 271 °C -
金型温度 38 - 66 °C -
Zone 1 238 °C -
Zone 2 249 °C -
Zone 3 254 °C -
Nozzle temperature 249 - 254 °C -
特殊な特性
成形加工法.
射出成形.
アプリケーション
自動車
領域別の利用可能性
北アメリカ., 南・中央アメリカ.
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com