Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of Rilsan® BESN BLACK P210 TL - PA11-I - ARKEMA

Material Data Center offers the following functions for Rilsan® BESN BLACK P210 TL:
unit conversion, PDF datasheet print, comparison with other plastics

Check here, which other Rilsan datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
機械的特性 - 熱的特性 - その他の特性.
Any use of this information falls under the rules of our disclaimer.
商品の説明文
PA11-HIP, EHL, 22-007
Rilsan® BESN BLACK P210 TL resin is a polyamide 11 produced from a renewable source. This black grade is plasticized and designed for extrusion.

Rilsan® BESN BLACK P210 TL resin falls into the PA11-PHLY category according to DIN 73378 and fulfills all specifications according to DIN 74324, ISO 7628, NFR 12632, and SAEJ844.

The biobased carbon content of Rilsan® BESN BLACK P210 TL resin is measured at 89% according to ASTM D6866.

Main applications:
  • Fluid transportation
  • Tubing for use in motor vehicle


Packaging:
This grade is delivered dried in sealed packaging (25 kg bags) ready to be processed.

Shelf Life:
Two years from the delivery. For any use above this limit, please refer to our technical services.
機械的特性乾燥/調湿単位テスト基準
ISO データ
引張弾性率 - / 600 MPa ISO 527
降伏応力 - / 32 MPa ISO 527
降伏ひずみ - / 31 % ISO 527
破壊呼びひずみ - / >50 % ISO 527
ノッチ付きシャルピー衝撃強さ, +23°C - / 76 kJ/m² ISO 179/1eA
ノッチ付きシャルピー衝撃強さ, -30°C - / 10 kJ/m² ISO 179/1eA
熱的特性乾燥/調湿単位テスト基準
ISO データ
溶融温度, 10°C/min 184 / * °C ISO 11357-1/-3
荷重たわみ温度, 1.80 MPa 45 / * °C ISO 75-1/-2
荷重たわみ温度, 0.45 MPa 110 / * °C ISO 75-1/-2
その他の特性.乾燥/調湿単位テスト基準
密度 1030 / 1030 kg/m³ ISO 1183
Biobased content 88 % -
特殊な特性
成形加工法.
異形押出成形., その他の押出成形.
納入形状.
ペレット., 黒
添加剤.
滑剤., 可塑剤.
特殊な特性.
高耐衝撃及び耐衝撃改良., 光安定化., 紫外線安定化., 熱安定化.
Certifications
Contains renewable resources
領域別の利用可能性
北アメリカ., ヨーロッパ., アジア/太平洋地域., 南・中央アメリカ., 近東/アフリカ
その他の情報
その他の押出成形.

Processing conditions:

- Typical melt temperature (Min / Recommended / Max) : 230°C / 250°C / 280°C.

- Drying time and temperature (only necessary for bags opened for more than two hours) : 4-8 hours at 80-90°C.
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com


Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.

Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.