Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of Ultradur® B 4406 - PBT FR(17) - BASF

Check here, which other Ultradur datasheets, application examples or technical articles are available in Material Data Center

Processing/Physical Characteristics - 機械的特性 - 熱的特性 - 電気的特性. - その他の特性. - 材料特有の特性 - Processing Recommendation Injection Molding - 機能

Any use of this information falls under the rules of our disclaimer.

商品の説明文

Injection molding grade with migration-free flame retardant; for parts requiring enhanced fire resistance (eg plug-and-socket connectors, housings).

Abbreviated designation according to ISO 1043: PBT FR(17)

Processing/Physical Characteristics	値	単位	テスト基準
ISO データ
メルトボリュームレイト, MVR	30	cm³/10min	ISO 1133
温度	275	°C	-
荷重	2.16	kg	-
成形収縮率, 平行	1.8	%	ISO 294-4, 2577
成形収縮率, 直角	1.9	%	ISO 294-4, 2577

機械的特性	値	単位	テスト基準
ISO データ
引張弾性率	3000	MPa	ISO 527
降伏応力	65	MPa	ISO 527
降伏ひずみ	3.9	%	ISO 527
破壊呼びひずみ	5.3	%	ISO 527
引張クリープ弾性率, 1h	1800	MPa	ISO 899-1
シャルピー衝撃強さ, +23°C	50	kJ/m²	ISO 179/1eU
ノッチ付きシャルピー衝撃強さ, +23°C	3.5	kJ/m²	ISO 179/1eA
ノッチ付きシャルピー衝撃強さ, -30°C	3.5	kJ/m²	ISO 179/1eA

熱的特性	値	単位	テスト基準
ISO データ
溶融温度, 10°C/min	223	°C	ISO 11357-1/-3
荷重たわみ温度, 1.80 MPa	60	°C	ISO 75-1/-2
荷重たわみ温度, 0.45 MPa	170	°C	ISO 75-1/-2
ビカット軟化温度, B	170	°C	ISO 306
線膨張係数, 平行	95	E-6/K	ISO 11359-1/-2
線膨張係数, 直角	103	E-6/K	ISO 11359-1/-2
1.5mm厚さでの燃焼性	V-0	class	IEC 60695-11-10
試験片の厚さ	1.6	mm	-
Yellow Card 可用	はい	-	-
厚さhでの燃焼性	V-0	class	IEC 60695-11-10
試験片の厚さ	0.4	mm	-
Yellow Card 可用	はい	-	-
酸素指数	29	%	ISO 4589-1/-2

電気的特性.	値	単位	テスト基準
ISO データ
比誘電率, 100Hz	3.3	-	IEC 62631-2-1
比誘電率, 1MHz	3.3	-	IEC 62631-2-1
誘電正接, 100Hz	110	E-4	IEC 62631-2-1
誘電正接, 1MHz	170	E-4	IEC 62631-2-1
体積抵抗率	1E13	Ohm*m	IEC 62631-3-1
表面抵抗率	1E14	Ohm	IEC 62631-3-2
耐電圧	40	kV/mm	IEC 60243-1
耐トラッキング性	250	-	IEC 60112

その他の特性.	値	単位	テスト基準
吸水率	0.4	%	Sim. to ISO 62
吸湿率	0.25	%	Sim. to ISO 62
密度	1450	kg/m³	ISO 1183

材料特有の特性	値	単位	テスト基準
ISO データ
粘度数	123	cm³/g	ISO 307, 1157, 1628

Processing Recommendation Injection Molding	値	単位	テスト基準
Pre-drying - Temperature	80 - 120	°C	-
Pre-drying - Time	4	h	-
Processing humidity	≤0.04	%	-
樹脂温度	245 - 270	°C	-
金型温度	40 - 70	°C	-

機能

特殊な特性

成形加工法.

射出成形.

納入形状.

ペレット.

添加剤.

滑剤.

特殊な特性.

難燃., 光安定化., 紫外線安定化., 熱安定化.

領域別の利用可能性

北アメリカ., ヨーロッパ., アジア/太平洋地域., 南・中央アメリカ., 近東/アフリカ

その他の情報

村遜速揃

PREPROCESSING
Pre/Post-processing, max. allowed water content: .04 %
Pre/Post-processing, Pre-drying, Temperature: 80 - 120 °C
Pre/Post-processing, Pre-drying, Time: 4 h

PROCESSING
injection molding, Melt temperature, range: 245 - 270 °C
injection molding, Melt temperature, recommended: 250 °C
injection molding, Mold temperature, range: 40 - 70 °C
injection molding, Mold temperature, recommended: 60 °C

Disclaimer

Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.

Created: Source: www.materialdatacenter.com