Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of VANDAR® 4662Z - PBT-GF30 - Celanese

Material Data Center offers the following functions for VANDAR® 4662Z:
unit conversion, PDF datasheet print, comparison with other plastics, snap fit calculation, beam deflection calculation, CAE Interfaces

Check here, which other Vandar datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Processing/Physical Characteristics - 機械的特性 - 熱的特性 - 電気的特性. - その他の特性. - 機能
Any use of this information falls under the rules of our disclaimer.
商品の説明文
Vandar 4662Zis a high impact polyester alloy which contains 30% glass fiber loading. It is characterized by toughness, dimensional stability, and high modulus. Good weatherability and moldability are other key attributes.

Flammability at thickness h (1.5 mm)HB-
Processing/Physical Characteristics値単位テスト基準
ISO データ
メルトボリュームレイト, MVR 5.5 cm³/10min ISO 1133
温度 250 °C -
荷重 5 kg -
成形収縮率, 平行 0.4 % ISO 294-4, 2577
成形収縮率, 直角 1.3 % ISO 294-4, 2577
機械的特性値単位テスト基準
ISO データ
引張弾性率 7000 MPa ISO 527
破壊応力 80 MPa ISO 527
破壊ひずみ 3.5 % ISO 527
シャルピー衝撃強さ, +23°C 70 kJ/m² ISO 179/1eU
シャルピー衝撃強さ, -30°C 70 kJ/m² ISO 179/1eU
ノッチ付きシャルピー衝撃強さ, +23°C 20 kJ/m² ISO 179/1eA
ノッチ付きシャルピー衝撃強さ, -30°C 10 kJ/m² ISO 179/1eA
熱的特性値単位テスト基準
ISO データ
溶融温度, 10°C/min 225 °C ISO 11357-1/-3
ガラス転移点, 10°C/min 60 °C ISO 11357-1/-2
荷重たわみ温度, 1.80 MPa 175 °C ISO 75-1/-2
荷重たわみ温度, 0.45 MPa 218 °C ISO 75-1/-2
ビカット軟化温度, B 190 °C ISO 306
線膨張係数, 平行 15 E-6/K ISO 11359-1/-2
線膨張係数, 直角 127 E-6/K ISO 11359-1/-2
厚さhでの燃焼性 HB class IEC 60695-11-10
試験片の厚さ 1.5 mm -
電気的特性.値単位テスト基準
ISO データ
比誘電率, 100Hz 4.9 - IEC 62631-2-1
比誘電率, 1MHz 4.3 - IEC 62631-2-1
誘電正接, 100Hz 70 E-4 IEC 62631-2-1
誘電正接, 1MHz 260 E-4 IEC 62631-2-1
体積抵抗率 1E12 Ohm*m IEC 62631-3-1
表面抵抗率 1E14 Ohm IEC 62631-3-2
耐電圧 33 kV/mm IEC 60243-1
その他の特性.値単位テスト基準
吸水率 0.45 % Sim. to ISO 62
吸湿率 0.2 % Sim. to ISO 62
密度 1470 kg/m³ ISO 1183
機能
せん断弾性率-温度. , VANDAR® 4662Z, PBT-GF30, Celanese
応力-ひずみ. , VANDAR® 4662Z, PBT-GF30, Celanese
割線弾性率−ひずみ. , VANDAR® 4662Z, PBT-GF30, Celanese
特殊な特性
成形加工法.
射出成形.
納入形状.
ペレット.
添加剤.
滑剤.
特殊な特性.
高耐衝撃及び耐衝撃改良., 紫外線安定化., 熱安定化.
領域別の利用可能性
北アメリカ., ヨーロッパ., アジア/太平洋地域., 南・中央アメリカ., 近東/アフリカ
その他の情報
村遜速揃
To avoid hydrolytic degradation during processing, Vandar resins have to be dried to a moisture level equal to or less than 0.02%. Drying should be done in a dehumidifying hopper dryer capable of dewpoints <-30°F (-34°C) at 250°F (121°C) for 4 hours.
Rear Temperature 450-480(230-250) deg F (deg C)
Center Temperature 460-490(235-255) deg F (deg C)
Front Temperature 470-500(240-260) deg F (deg C)
Nozzle Temperature 470-510(240-265) deg F (deg C)
Melt Temperature 470-510(240-265) deg F (deg C)
Mold Temperature 100-200(40-95 deg F (deg C)
Back Pressure 0-50 psi
Screw Speed Moderate
Injection Speed Fast

Injection speed, injection pressure and holding pressure have to be optimized to the individual article geometry. To avoid material degradation during processing low back pressure and minimum screw speed have to be used. Overheating of the material has to be avoided, in particular for flame retardant grades. Up to 25% clean and dry regrind may be used.
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com


Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.

Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.