Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of Fiberfil® J-62/30/E - PP-GF30 - LyondellBasell Industries

Material Data Center offers the following functions for Fiberfil® J-62/30/E:
unit conversion, PDF datasheet print, comparison with other plastics

Check here, which other Fiberfil datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Processing/Physical Characteristics - 機械的特性 - 熱的特性 - その他の特性. - Processing Recommendation Injection Molding
Any use of this information falls under the rules of our disclaimer.
Processing/Physical Characteristics値単位テスト基準
ASTM数据
メルトフローレイト, MFI 7 g/10min ASTM D 1238
温度 230 °C -
荷重 2.16 kg -
成形収縮率., 平行 0.0025 mm/mm ASTM D 955
機械的特性値単位テスト基準
ASTM数据
引張弾性率 4830 MPa ASTM D 638
引張強度 60.7 MPa ASTM D 638
降伏点伸び 3.7 % ASTM D 638
曲げ弾性率 4480 MPa ASTM D 790
曲げ強さ 100 MPa ASTM D 790
ロックウェル硬度 R 95 - ASTM D 785
ノッチ付きIzod衝撃強さ, 1/8 in 130 J/m ASTM D 256
熱的特性値単位テスト基準
ASTM数据
DTUL @ 66 psi 136 °C ASTM D 648
DTUL @ 264 psi 146 °C ASTM D 648
その他の特性.値単位テスト基準
吸水率, 24hr 0.03 % ASTM D 570
密度 1120 kg/m³ ASTM D 792
Processing Recommendation Injection Molding値単位テスト基準
Pre-drying - Temperature 77 °C -
Pre-drying - Time 2 h -
Processing humidity ≤0.2 % -
樹脂温度 199 - 232 °C -
金型温度 32 - 71 °C -
Zone 1 199 - 210 °C -
Zone 2 204 - 227 °C -
Zone 3 182 - 199 °C -
Nozzle temperature 182 - 193 °C -
Back pressure 0 - 0.689 MPa -
特殊な特性
成形加工法.
射出成形.
納入形状.
ペレット.
な特性
Chemically Coupled Reinforcement, Copolymer
領域別の利用可能性
北アメリカ.
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com