商品の説明文
KURARITY is non-crystalline block copolymer and does not have melting point.
All the KURARITY grades show similar low temperature properties which result from Tg of
poly (n-butyl acrylate) or poly (n-butyl acrylate/2-ethylhexyl acrylate) and heat resistance
from Tg of PMMA.
LA series : n-butyl acrylate based block copolymers.
Suitable Applications: For Molding, Compound, Additives.
| Processing/Physical Characteristics | 値 | 単位 | テスト基準 |
| ISO データ |
| メルトフローレート, MFI |
1.5 |
g/10min |
ISO 1133 |
| 温度 |
190 |
°C |
- |
| 荷重 |
2.16 |
kg |
- |
| 機械的特性 | 値 | 単位 | テスト基準 |
| ISO データ |
| 引張強度 |
17 |
MPa |
ISO 527 |
| 曲げ弾性率, 23°C |
750 |
MPa |
ISO 178 |
| ノッチ付きシャルピー衝撃強さ, +23°C |
30 |
kJ/m² |
ISO 179/1eA |
| 引張強度 |
25 |
MPa |
ISO 37 |
| ショア硬さA |
90 |
- |
ISO 7619-1 |
| ショア硬さD |
47 |
- |
ISO 7619-1 |
| Other Standards[S] |
| 伸び率100%時の応力 |
19 |
MPa |
ISO 37 |
| S: | These properties are reported by the producer according standards that are different to our defaults. |
| 熱的特性 | 値 | 単位 | テスト基準 |
| Other Standards[S] |
| 熱伝導率, ソリッド |
0.17 |
W/(m K) |
ASTM E 1530 |
| S: | These properties are reported by the producer according standards that are different to our defaults. |
| 電気的特性. | 値 | 単位 | テスト基準 |
| Other Standards[S] |
| 誘電正接, 60 Hz |
0.0394 |
- |
JIS C 2138 |
| 誘電正接, 1 MHz |
0.0448 |
- |
JIS C 2138 |
| 比誘電率, 60 Hz |
4.56 |
- |
JIS C 2138 |
| 比誘電率, 1 MHz |
3.68 |
- |
JIS C 2138 |
| S: | These properties are reported by the producer according standards that are different to our defaults. |
| 光学特性 | 値 | 単位 | テスト基準 |
| ISO Data |
| ヘイズ |
2 |
- |
ISO 14782 |
| Other Standards[S] |
| 視感透過率 |
93 |
% |
ISO 13468-1 |
| S: | These properties are reported by the producer according standards that are different to our defaults. |
| その他の特性. | 値 | 単位 | テスト基準 |
| 密度. |
1120 |
kg/m³ |
ISO 1183 |
| Processing Recommendation Injection Molding | 値 | 単位 | テスト基準 |
| Pre-drying - Temperature |
70 - 80 |
°C |
- |
| Pre-drying - Time |
4 |
h |
- |
| 樹脂温度 |
200 - 230 |
°C |
- |
| 金型温度 |
20 - 40 |
°C |
- |
| Screw speed |
<100 |
rpm |
- |
| Back pressure |
0 - 5 |
MPa |
- |
特殊な特性
成形加工法.
射出成形.
納入形状.
ペレット.
特殊な特性.
紫外線安定化., 透明.
な特性
Blending Resin, Low Odor, Copolymer
耐薬品性
Acid Resistance, Alkali Resistance, Oil Resistance
アプリケーション
自動車, 電気電子
領域別の利用可能性
北アメリカ., ヨーロッパ., アジア/太平洋地域.
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com