Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of LEONA™ CR302 - PA66-MF - Asahi Kasei

Material Data Center offers the following functions for LEONA™ CR302:
unit conversion, PDF datasheet print, comparison with other plastics, snap fit calculation, beam deflection calculation, CAE Interfaces

Check here, which other Leona datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Any use of this information falls under the rules of our disclaimer.
機械的特性乾燥/調湿単位テスト基準
ISO データ
引張弾性率 10000 / 7600 MPa ISO 527
破壊応力 140 / 92 MPa ISO 527
破壊ひずみ 2 / 2.5 % ISO 527
曲げ弾性率, 23°C 9800 / 7100 MPa ISO 178
曲げ強さ 197 / 148 MPa ISO 178
シャルピー衝撃強さ, +23°C 38 / 46 kJ/m² ISO 179/1eU
ノッチ付きシャルピー衝撃強さ, +23°C 4 / 5 kJ/m² ISO 179/1eA
ロックウェル硬度 M 90 - ISO 2039-2
ASTM数据
引張強度 128 / 98 MPa ASTM D 638
破断伸び 3 / 3.5 % ASTM D 638
曲げ弾性率 8800 / 5800 MPa ASTM D 790
曲げ強さ 191 / 157 MPa ASTM D 790
ロックウェル硬度 M 90 / - ASTM D 785
ノッチ付きIzod衝撃強さ, 1/8 in 36 / 39 J/m ASTM D 256
熱的特性乾燥/調湿単位テスト基準
ISO データ
荷重たわみ温度, 1.80 MPa 247 / * °C ISO 75-1/-2
荷重たわみ温度, 0.45 MPa 260 / * °C ISO 75-1/-2
厚さhでの燃焼性 HB / * class IEC 60695-11-10
Yellow Card 可用 はい / * - -
ASTM数据
UL94 燃焼性 HB - UL 94
追加試験片の厚さ 0.75 mm -
DTUL @ 66 psi 250 °C ASTM D 648
DTUL @ 264 psi 245 °C ASTM D 648
その他の特性.乾燥/調湿単位テスト基準
吸湿率 1.4 / * % Sim. to ISO 62
密度 1520 / - kg/m³ ISO 1183
密度 1520 kg/m³ ASTM D 792
Processing Recommendation Injection Molding単位テスト基準
Pre-drying - Temperature 80 - 90 °C -
Pre-drying - Time 2 - 3 h -
樹脂温度 275 - 295 °C -
金型温度 75 - 85 °C -
特殊な特性
成形加工法.
射出成形.
納入形状.
ペレット.
特殊な特性.
熱安定化.
領域別の利用可能性
北アメリカ., ヨーロッパ., アジア/太平洋地域., 南・中央アメリカ., 近東/アフリカ
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com