Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.
This is the free Material Data Center Datasheet of LUPOY HR5007AX - (PC+ABS) - LG Chem
Material Data Center offers the following functions for LUPOY HR5007AX:
unit conversion, PDF datasheet print, comparison with other plastics, snap fit calculation, beam deflection calculation, CAE Interfaces
Check here, which other Lupoy datasheets, application examples or technical articles are available in Material Data Center
Use the following short links to get directly to the properties of interest in this datasheet:
Any use of this information falls under the rules of our
disclaimer.
| Processing/Physical Characteristics | 値 | 単位 | テスト基準 |
| ISO データ |
| メルトフローレート, MFI |
15 |
g/10min |
ISO 1133 |
| 温度 |
260 |
°C |
- |
| 荷重 |
5 |
kg |
- |
| 成形収縮率, 平行 |
0 |
% |
ISO 294-4, 2577 |
| 成形収縮率, 直角 |
0 |
% |
ISO 294-4, 2577 |
| ASTM数据 |
| メルトフローレイト, MFI |
2.6 |
g/10min |
ASTM D 1238 |
| 温度 |
250 |
°C |
- |
| 荷重 |
2.16 |
kg |
- |
| 成形収縮率., 平行 |
0.0065 |
mm/mm |
ASTM D 955 |
| 成形収縮率, 直角 |
0.0075 |
mm/mm |
ASTM D 955 |
| 機械的特性 | 値 | 単位 | テスト基準 |
| ISO データ |
| 引張弾性率 |
2040 |
MPa |
ISO 527 |
| 降伏応力 |
50 |
MPa |
ISO 527 |
| 降伏ひずみ |
5.4 |
% |
ISO 527 |
| 破壊応力 |
48 |
MPa |
ISO 527 |
| 破壊ひずみ |
100 |
% |
ISO 527 |
| 曲げ弾性率, 23°C |
2070 |
MPa |
ISO 178 |
| 曲げ強さ |
78 |
MPa |
ISO 178 |
| ノッチ付きシャルピー衝撃強さ, +23°C |
52[1] |
kJ/m² |
ISO 179/1eA |
| ノッチ付きシャルピー衝撃強さ, -30ﾟC |
27[1] |
kJ/m² |
ISO 179/1eA |
| ノッチ付きIzod衝撃強さ, +23°C |
50[1] |
kJ/m² |
ISO 180/1A |
| ノッチ付きIzod衝撃強さ |
23[1] |
kJ/m² |
ISO 180/1A |
| 温度 |
-40 |
°C |
- |
| ロックウェル硬度 |
R 112 |
- |
ISO 2039-2 |
| ASTM数据 |
| 引張弾性率 |
1978 |
MPa |
ASTM D 638 |
| 降伏応力 |
53 |
MPa |
ASTM D 638 |
| 破壊応力 |
53 |
MPa |
ASTM D 638 |
| 降伏点伸び |
5.3 |
% |
ASTM D 638 |
| 破断伸び |
110 |
% |
ASTM D 638 |
| 曲げ弾性率 |
2109 |
MPa |
ASTM D 790 |
| 曲げ強さ |
81.4 |
MPa |
ASTM D 790 |
| ロックウェル硬度 |
R 112 |
- |
ASTM D 785 |
| ノッチ付きIzod衝撃強さ, 1/8 in |
618 |
J/m |
ASTM D 256 |
| ノッチ付きIzod衝撃強さ, 1/4 in |
471 |
J/m |
ASTM D 256 |
| ノッチ付きIzod衝撃強さ, Low-Temperature |
402 |
J/m |
ASTM D 256 |
| 温度 |
-30 |
°C |
- |
| 熱的特性 | 値 | 単位 | テスト基準 |
| ISO データ |
| 荷重たわみ温度, 1.80 MPa |
105[2] |
°C |
ISO 75-1/-2 |
| 荷重たわみ温度, 0.45 MPa |
127[2] |
°C |
ISO 75-1/-2 |
| ビカット軟化温度, B |
124 |
°C |
ISO 306 |
| 線膨張係数, 平行 |
77 |
E-6/K |
ISO 11359-1/-2 |
| 線膨張係数, 直角 |
92 |
E-6/K |
ISO 11359-1/-2 |
| 厚さhでの燃焼性 |
HB |
class |
IEC 60695-11-10 |
| 試験片の厚さ |
0.8 |
mm |
- |
| ASTM数据 |
| UL94 燃焼性 |
HB |
- |
UL 94 |
| 追加試験片の厚さ |
0.76 |
mm |
- |
| 線膨張係数, 平行 |
77 |
E-6/K |
ASTM D 696 |
| 線膨張係数, 直角 |
92 |
E-6/K |
ASTM D 696 |
| DTUL @ 66 psi |
133[3] |
°C |
ASTM D 648 |
| DTUL @ 264 psi |
116[3] |
°C |
ASTM D 648 |
| ビカット軟化温度 |
130 |
°C |
ASTM D 1525 |
| 電気的特性. | 値 | 単位 | テスト基準 |
| ISO データ |
| 体積抵抗率 |
1E15 |
Ohm*m |
IEC 62631-3-1 |
| 表面抵抗率 |
1E15 |
Ohm |
IEC 62631-3-2 |
| 耐トラッキング性 |
600 |
- |
IEC 60112 |
| ASTM数据 |
| 耐電圧, 短い時間 |
21 |
kV/mm |
ASTM D 149 |
| 表面抵抗率 |
1E15 |
Ohm |
ASTM D 257 |
| 体積抵抗率 |
1E17 |
Ohm*cm |
ASTM D 257 |
| その他の特性. | 値 | 単位 | テスト基準 |
| 吸湿率 |
0.2 |
% |
Sim. to ISO 62 |
| 密度. |
1140 |
kg/m³ |
ISO 1183 |
| 密度 |
1140 |
kg/m³ |
ASTM D 792 |
| Processing Recommendation Injection Molding | 値 | 単位 | テスト基準 |
| Pre-drying - Temperature |
80 - 100 |
°C |
- |
| Pre-drying - Time |
4 - 6 |
h |
- |
| Processing humidity |
≤0.02 |
% |
- |
| 樹脂温度 |
250 - 275 |
°C |
- |
| 金型温度 |
50 - 70 |
°C |
- |
| Zone 1 |
240 - 270 |
°C |
- |
| Zone 2 |
245 - 275 |
°C |
- |
| Zone 3 |
245 - 285 |
°C |
- |
| Nozzle temperature |
245 - 275 |
°C |
- |
特殊な特性
成形加工法.
射出成形.
特殊な特性.
熱安定化.
アプリケーション
電気電子, 汎用
領域別の利用可能性
北アメリカ., ヨーロッパ., アジア/太平洋地域., 南・中央アメリカ.
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com