Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of MAGNUM™ 357 HP - ABS - Trinseo

Material Data Center offers the following functions for MAGNUM™ 357 HP:
unit conversion, PDF datasheet print, comparison with other plastics, cooling time calculation, CAE Interfaces

Check here, which other Magnum datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Processing/Physical Characteristics - 機械的特性 - 熱的特性 - その他の特性. - Processing Recommendation Injection Molding
Any use of this information falls under the rules of our disclaimer.
Processing/Physical Characteristics値単位テスト基準
ISO データ
溶融時の密度 1080 kg/m³ -
溶融時の熱伝導率 0.13 W/(m K) -
溶融時の比熱 1890 J/(kg K) -
突き出し時の時の温度 127 °C -
ASTM数据
メルトフローレイト, MFI 2 g/10min ASTM D 1238
温度 230 °C -
荷重 3.8 kg -
成形収縮率., 平行 0.0055 mm/mm ASTM D 955
機械的特性値単位テスト基準
ASTM数据
引張弾性率 1999 MPa ASTM D 638
降伏応力 37.9 MPa ASTM D 638
破壊応力 33.1 MPa ASTM D 638
破断伸び 45 % ASTM D 638
曲げ弾性率 2206 MPa ASTM D 790
曲げ強さ 62.1 MPa ASTM D 790
ノッチ付きIzod衝撃強さ, 1/8 in 310 J/m ASTM D 256
ノッチ付きIzod衝撃強さ, Low-Temperature 128 J/m ASTM D 256
温度 -17.8 °C -
熱的特性値単位テスト基準
ASTM数据
線膨張係数, 平行 81 E-6/K ASTM D 696
DTUL @ 66 psi 104 °C ASTM D 648
DTUL @ 264 psi 87.8 °C ASTM D 648
ビカット軟化温度 120 °C ASTM D 1525
その他の特性.値単位テスト基準
密度 1060 kg/m³ ASTM D 792
Processing Recommendation Injection Molding値単位テスト基準
Pre-drying - Temperature 82.2 - 85 °C -
Pre-drying - Time 2 - 4 h -
Processing humidity ≤0.1 % -
樹脂温度 260 - 282 °C -
金型温度 37.8 - 82.2 °C -
Back pressure 0.345 - 0.689 MPa -
特殊な特性
成形加工法.
射出成形., 異形押出成形., シート押出成形., 熱成形.
特殊な特性.
熱安定化.
アプリケーション
自動車
領域別の利用可能性
北アメリカ., 南・中央アメリカ.
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com


Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.

Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.