Complete Set of CAMPUS® Data, ASTM Data, Biopolymer Database, Application Database, Tradename Database, Literature Database, Toolbox.

Material datasheets available free. Online registration at: www.materialdatacenter.com

Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of SCHULAMID® 6 MT 30 - PA6-T30 - LyondellBasell Industries

Material Data Center offers the following functions for SCHULAMID® 6 MT 30:
unit conversion, PDF datasheet print, comparison with other plastics, snap fit calculation, beam deflection calculation, parameters for material models, CAE Interfaces

Check here, which other Schulamid datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
기계적 특성 - 열적 특성 - 기타 특성 - 물질의 비성질 - Processing Recommendation Injection Molding - 도표
Any use of this information falls under the rules of our disclaimer.
제품 설명서
30% talc filled PA 6 grade

기계적 특성건조/응축단위시험규격
ISO 데이터
인장탄성률 6500 / 3300 MPa ISO 527
파단시 강도 70 / 45 MPa ISO 527
파단시 신율 3.5 / 15 % ISO 527
챠피 충격 강도 , +23°C 35 / 60 kJ/m² ISO 179/1eU
챠피 충격 강도, -30°C 30 / - kJ/m² ISO 179/1eU
챠피 노치드 충격 강도, +23°C 4 / 8 kJ/m² ISO 179/1eA
챠피 노치드 충격 강도, -30°C 3 / - kJ/m² ISO 179/1eA
열적 특성건조/응축단위시험규격
ISO 데이터
하중하에서의 변형온도, 1.80 MPa 100 / * °C ISO 75-1/-2
하중하에서의 변형온도, 0.45 MPa 200 / * °C ISO 75-1/-2
비카트 연화 온도, B 200 / * °C ISO 306
연소속도, FMVSS, 두께 1mm 100 mm/min ISO 3795 (FMVSS 302)
기타 특성건조/응축단위시험규격
밀도 1360 / - kg/m³ ISO 1183
물질의 비성질건조/응축단위시험규격
ISO 데이터
점도수 140 / * cm³/g ISO 307, 1157, 1628
Processing Recommendation Injection Molding값단위시험규격
Pre-drying - Temperature 80 °C -
Pre-drying - Time 4 - 6 h -
용융수지온도 250 - 280 °C -
성형온도 60 - 90 °C -
도표
점도-변형률 , SCHULAMID® 6 MT 30, PA6-T30, LyondellBasell
전단-변형률 , SCHULAMID® 6 MT 30, PA6-T30, LyondellBasell
특징
생산 공정
사출 성형
인도 유형
과립
부가물
이형제
지역별 검색
쨘횕쩐횈쨍횧쨍짰횆짬, 짱쨌쨈, 쩐횈쩍횄쩐횈 횇횂횈챵쩐챌 횁철쩔짧, 쨀짼쨘횓 쨔횞 횁횩쩐횙 쩐횈쨍횧쨍짰횆짬, 쨉쩔쩐챌 쨔횞 쩐횈횉횁쨍짰횆짬 짹횢쩔짧
기타 정보
사E성
PREPROCESSING; Pretreatment
Predrying: 4-6h / 80°C

PROCESSING ;Processing:

Melttemperature250 - 280°C
Mouldtemperature60 - 90°C
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com


Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.

Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.