Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of SCHULAMID® 6 MV 14 FR 4 K1681 - PA6 - LyondellBasell Industries

Check here, which other Schulamid datasheets, application examples or technical articles are available in Material Data Center

기계적 특성 - 열적 특성 - 전기적 특성 - 기타 특성 - 물질의 비성질 - Processing Recommendation Injection Molding - 도표

Any use of this information falls under the rules of our disclaimer.

제품 설명서

Flame retardant PA 6 grade (V-2); incandescent wire test without flame; GWIT at 825°C; without PBDE

기계적 특성	건조/응축	단위	시험규격
ISO 데이터
인장탄성률	3800 / 1250	MPa	ISO 527
항복강도	70 / 35	MPa	ISO 527
항복변형률	3 / 24	%	ISO 527
챠피 충격 강도 , +23°C	49 / N	kJ/m²	ISO 179/1eU
챠피 충격 강도, -30°C	48 / -	kJ/m²	ISO 179/1eU
챠피 노치드 충격 강도, +23°C	4 / 18	kJ/m²	ISO 179/1eA
챠피 노치드 충격 강도, -30°C	3 / -	kJ/m²	ISO 179/1eA

열적 특성	건조/응축	단위	시험규격
ISO 데이터
하중하에서의 변형온도, 1.80 MPa	76 / *	°C	ISO 75-1/-2
하중하에서의 변형온도, 0.45 MPa	186 / *	°C	ISO 75-1/-2
비카트 연화 온도, B	202 / *	°C	ISO 306
1.5mm 평균두께에서의 난연성	V-2 / *	class	IEC 60695-11-10
두께 H인 제품의 난연성	V-2 / *	class	IEC 60695-11-10
테스트 두께	3.0 / *	mm	-
Yellow Card 유효한	예 / *	-	-
산소지수로서의 난연성	23 / *	%	ISO 4589-1/-2
ASTM 데이터
UL94 난연성	V-2	-	UL 94
테스트 두께	1.5	mm	-

전기적 특성	건조/응축	단위	시험규격
ISO 데이터
CTI	300 / -	-	IEC 60112

기타 특성	건조/응축	단위	시험규격
밀도	1260 / -	kg/m³	ISO 1183

물질의 비성질	건조/응축	단위	시험규격
ISO 데이터
점도수	145 / *	cm³/g	ISO 307, 1157, 1628

Processing Recommendation Injection Molding	값	단위	시험규격
Pre-drying - Temperature	80	°C	-
Pre-drying - Time	4 - 6	h	-
용융수지온도	230 - 240	°C	-
성형온도	60 - 90	°C	-

도표

특징

생산 공정

사출 성형, 중공 성형

인도 유형

과립

부가물

이형제

특별 특성

난연성

지역별 검색

쨘횕쩐횈쨍횧쨍짰횆짬, 짱쨌쨈, 쩐횈쩍횄쩐횈 횇횂횈챵쩐챌 횁철쩔짧, 쨀짼쨘횓 쨔횞 횁횩쩐횙 쩐횈쨍횧쨍짰횆짬, 쨉쩔쩐챌 쨔횞 쩐횈횉횁쨍짰횆짬 짹횢쩔짧

기타 정보

사E성

PREPROCESSING; Pretreatment
Predrying: 4-6h / 80°C

PROCESSING ;Processing:

Melttemperature	230 - 240	°C
Mouldtemperature	60 - 90	°C

Disclaimer

Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.

Created: Source: www.materialdatacenter.com

Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.

Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.