Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of Ultradur® B 4520 - PBT - BASF

Check here, which other Ultradur datasheets, application examples or technical articles are available in Material Data Center

Processing/Physical Characteristics - 기계적 특성 - 열적 특성 - 전기적 특성 - 기타 특성 - 물질의 비성질 - Processing Recommendation Injection Molding - Processing Recommendation Extrusion - 도표

Any use of this information falls under the rules of our disclaimer.

제품 설명서

Standard injection molding grade for the production of various functional parts.
The products can also be offered as BMBcert™ and/or Ccycled™. Due to the Massbalance approach the product properties do not change

Abbreviated designation according to ISO 1043-1: PBT

Processing/Physical Characteristics	값	단위	시험규격
ISO 데이터
용융 부피 - 흐름 속도, MVR	20	cm³/10min	ISO 1133
온도	250	°C	-
하중	2.16	kg	-
성형 수축률, 평행	1.7	%	ISO 294-4, 2577
성형 수축률, 수직	1.7	%	ISO 294-4, 2577
ASTM 데이터
성형 수축률, 평행	0.015	mm/mm	ASTM D 955

기계적 특성	값	단위	시험규격
ISO 데이터
인장탄성률	2400	MPa	ISO 527
항복강도	55	MPa	ISO 527
항복변형률	3.7	%	ISO 527
파단시 평균신율	>50	%	ISO 527
굴곡 계수, 23°C	2400	MPa	ISO 178
굴곡 강도	85	MPa	ISO 178
탄성변형률, 1h	1800	MPa	ISO 899-1
탄성변형률, 1000h	1200	MPa	ISO 899-1
챠피 충격 강도 , +23°C	N	kJ/m²	ISO 179/1eU
챠피 충격 강도, -30°C	180	kJ/m²	ISO 179/1eU
챠피 노치드 충격 강도, +23°C	5	kJ/m²	ISO 179/1eA
챠피 노치드 충격 강도, -30°C	3	kJ/m²	ISO 179/1eA
Ball indentation hardness	130	MPa	ISO 2039-1
ASTM 데이터
인장탄성률	2482	MPa	ASTM D 638
항복강도	60	MPa	ASTM D 638
항복변형률	3.7	%	ASTM D 638
굴곡 계수	2303	MPa	ASTM D 790

열적 특성	값	단위	시험규격
ISO 데이터
녹는점, 10°C/min	223	°C	ISO 11357-1/-3
하중하에서의 변형온도, 1.80 MPa	55	°C	ISO 75-1/-2
하중하에서의 변형온도, 0.45 MPa	165	°C	ISO 75-1/-2
선형 열팽창 계수, 평행	115	E-6/K	ISO 11359-1/-2
선형 열팽창 계수, 수직	115	E-6/K	ISO 11359-1/-2
1.5mm 평균두께에서의 난연성	HB	class	IEC 60695-11-10
테스트 두께	1.5	mm	-
Yellow Card 유효한	예	-	-
두께 H인 제품의 난연성	HB	class	IEC 60695-11-10
테스트 두께	0.8	mm	-
Yellow Card 유효한	예	-	-
산소지수로서의 난연성	20	%	ISO 4589-1/-2
ASTM 데이터
DTUL @ 66 psi	163	°C	ASTM D 648
DTUL @ 264 psi	60	°C	ASTM D 648
녹는점	223	°C	ASTM D 3418

전기적 특성	값	단위	시험규격
ISO 데이터
상대 유전율, 100Hz	3.4	-	IEC 62631-2-1
상대 유전뮬, 1MHz	3.3	-	IEC 62631-2-1
소산 인자, 100Hz	20	E-4	IEC 62631-2-1
소산 인자, 1MHz	200	E-4	IEC 62631-2-1
부피 저항	>1E13	Ohm*m	IEC 62631-3-1
표면 저항	1E13	Ohm	IEC 62631-3-2
전기 압력	36	kV/mm	IEC 60243-1
CTI	550	-	IEC 60112

기타 특성	값	단위	시험규격
물에서의 흡수성	0.5	%	ISO 62와 유사
조건에서의 흡습성	0.25	%	ISO 62와 유사
밀도	1300	kg/m³	ISO 1183
Bulk density	750	kg/m³	-
밀도	1680	kg/m³	ASTM D 792

물질의 비성질	값	단위	시험규격
ISO 데이터
점도수	130	cm³/g	ISO 307, 1157, 1628

Processing Recommendation Injection Molding	값	단위	시험규격
Processing humidity	≤0.04	%	-
용융수지온도	250 - 275	°C	-
성형온도	40 - 70	°C	-

Processing Recommendation Extrusion	값	단위	시험규격
Processing humidity	≤0.04	%	-
용융수지온도	250 - 275	°C	-

도표

특징

생산 공정

사출 성형, 기타 압출

인도 유형

펠렛 (입자,알갱이), 검정, 자연 색상

부가물

윤활제

특별 특성

가시광선 안정성, U.V. 안정성 또는 기후 안정성, 열안정성

응용

자동차의

지역별 검색

쨘횕쩐횈쨍횧쨍짰횆짬, 짱쨌쨈, 쩐횈쩍횄쩐횈 횇횂횈챵쩐챌 횁철쩔짧, 쨀짼쨘횓 쨔횞 횁횩쩐횙 쩐횈쨍횧쨍짰횆짬, 쨉쩔쩐챌 쨔횞 쩐횈횉횁쨍짰횆짬 짹횢쩔짧

기타 정보

사E성

PREPROCESSING
Pre/Post-processing, max. allowed water content: .04 %
Pre/Post-processing, Pre-drying, Temperature: 80 - 120 °C
Pre/Post-processing, Pre-drying, Time: 4 h

PROCESSING
injection molding, Melt temperature, range: 250 - 275 °C
injection molding, Melt temperature, recommended: 260 °C
injection molding, Mold temperature, range: 40 - 70 °C
injection molding, Mold temperature, recommended: 60 °C

화학적 매체에 대한 저항력

산
	에서의 아세트산 (질량 5%) (23°C)
	23 °C에서의 시트르산 용액 (질량 10%) (23°C)
	23 °C에서의 락트산 (질량 10%) (23°C)
염기
	에서의 수산화나트륨 용액 (질량 35%) (23°C)
	에서의 수산화암모늄 용액 (질량 10%) (23°C)
알코올
	23 °C에서의 이소프로필 알코올 (23°C)
	23 °C에서의 메탄올 (23°C)
	23 °C에서의 에탄올 (23°C)
탄화수소
	에서의 n-헥산 (23°C)
	에서의 톨루엔 (23°C)
	에서의 이소옥탄 (23°C)
케톤
	에서의 아세톤 (23°C)
에테르
	에서의 디에틸 에테르 (23°C)
광유
	에서의 SAE 10W40 멀티그레이드 모터 오일 (23°C)
	에서의 SAE 10W40 멀티그레이드 모터 오일 (130°C)
표준 연료
	에서의 디젤 연료 (ISO 1817 액체 F 참조) (23°C)
염액
	에서의 탄산나트륨 용액 (질량 2%) (23°C)
기타
	에서의 초산 에틸 (23°C)
	에서의 물 (23°C)

Disclaimer

Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.

Created: Source: www.materialdatacenter.com