Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of Vydyne® R530HR BK652 - PA66-GF30 - Ascend

Material Data Center offers the following functions for Vydyne® R530HR BK652:
unit conversion, PDF datasheet print, snap fit calculation, beam deflection calculation, CAE Interfaces

Check here, which other Vydyne datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Processing/Physical Characteristics - 기계적 특성 - 열적 특성 - 기타 특성 - Processing Recommendation Injection Molding
Any use of this information falls under the rules of our disclaimer.
제품 설명서
Vydyne R530HR BK0652 is a 30% glass-filled, heat-stabilized PA66 based resin designed for injection molding applications. It was specifically developed to withstand long term exposure to coolants at temperatures up to 135°C. R530HR BK0652 offers improved flow with a black surface finish and maintains the excellent resistance typical of PA66 in chemicals, machine and motor oils, solvents, and gasoline.
Processing/Physical Characteristics건조/응축단위시험규격
ISO 데이터
성형 수축률, 평행 0.5 / * % ISO 294-4, 2577
성형 수축률, 수직 1.2 / * % ISO 294-4, 2577
기계적 특성건조/응축단위시험규격
ISO 데이터
인장탄성률 10100 / 7300 MPa ISO 527
파단시 강도 179 / 126 MPa ISO 527
파단시 신율 3.8 / 7 % ISO 527
굴곡 계수, 23°C 9500 / 6000 MPa ISO 178
굴곡 강도 265 / 155 MPa ISO 178
챠피 충격 강도 , +23°C 87 / 103 kJ/m² ISO 179/1eU
챠피 충격 강도, -30°C 70 / 84 kJ/m² ISO 179/1eU
챠피 노치드 충격 강도, +23°C 12 / 17 kJ/m² ISO 179/1eA
챠피 노치드 충격 강도, -30°C 11 / 11 kJ/m² ISO 179/1eA
아이조드 충격은 노치, +23°C 14 / 17 kJ/m² ISO 180/1A
아이조드 충격은 노치 11 / 13 kJ/m² ISO 180/1A
온도 -40 °C -
열적 특성건조/응축단위시험규격
ISO 데이터
녹는점, 10°C/min 260 / * °C ISO 11357-1/-3
하중하에서의 변형온도, 1.80 MPa 249 / * °C ISO 75-1/-2
하중하에서의 변형온도, 0.45 MPa 260 / * °C ISO 75-1/-2
선형 열팽창 계수, 평행 23 / * E-6/K ISO 11359-1/-2
선형 열팽창 계수, 수직 81 / * E-6/K ISO 11359-1/-2
기타 특성건조/응축단위시험규격
물에서의 흡수성 1 / * % ISO 62와 유사
조건에서의 흡습성 1.9 / * % ISO 62와 유사
밀도 1370 / - kg/m³ ISO 1183
Processing Recommendation Injection Molding값단위시험규격
Pre-drying - Temperature 80 °C -
Pre-drying - Time 4 h -
용융수지온도 285 - 305 °C -
성형온도 65 - 95 °C -
Zone 1 280 - 310 °C -
Zone 2 280 - 310 °C -
Zone 3 280 - 310 °C -
Nozzle temperature 280 - 310 °C -
특징
생산 공정
사출 성형
인도 유형
펠렛 (입자,알갱이), 검정
부가물
윤활제
특별 특성
열안정성
특성
Fatigue Resistance
내화학성에
General Chemical Resistance, Solvent Resistance, Hydrolytically Stable, Oil Resistance
응용
자동차의
지역별 검색
쨘횕쩐횈쨍횧쨍짰횆짬, 짱쨌쨈, 쩐횈쩍횄쩐횈 횇횂횈챵쩐챌 횁철쩔짧
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com