Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.
This is the free Material Data Center Datasheet of LUPOY GN5001RFG - (PC+ABS) - LG Chem
Material Data Center offers the following functions for LUPOY GN5001RFG:
unit conversion, PDF datasheet print, comparison with other plastics, snap fit calculation, beam deflection calculation, CAE Interfaces
Check here, which other Lupoy datasheets, application examples or technical articles are available in Material Data Center
Use the following short links to get directly to the properties of interest in this datasheet:
Any use of this information falls under the rules of our
disclaimer.
| 加工/物理特性 | 价值 | 单位 | Test Standard |
| ISO数据 |
| 熔融指数, MFI |
21 |
g/10min |
ISO 1133 |
| 温度 |
250 |
°C |
- |
| 负载 |
2.16 |
kg |
- |
| 模塑收缩率, 平行 |
0 |
% |
ISO 294-4, 2577 |
| 模塑收缩率, 垂直 |
0 |
% |
ISO 294-4, 2577 |
| ASTM数据 |
| 熔融指数, MFI |
21 |
g/10min |
ASTM D 1238 |
| 温度 |
250 |
°C |
- |
| 负载 |
2.16 |
kg |
- |
| 模压收缩率, 平行 |
0.005 |
mm/mm |
ASTM D 955 |
| 模压收缩率, TD |
0.005 |
mm/mm |
ASTM D 955 |
| 机械性能 | 价值 | 单位 | Test Standard |
| ISO数据 |
| 拉伸模量 |
2570 |
MPa |
ISO 527 |
| 屈服应力 |
58 |
MPa |
ISO 527 |
| 屈服伸长率 |
4 |
% |
ISO 527 |
| 断裂应力 |
49 |
MPa |
ISO 527 |
| 断裂伸长率 |
75 |
% |
ISO 527 |
| 弯曲模量, 23°C |
2500 |
MPa |
ISO 178 |
| 弯曲强度 |
90 |
MPa |
ISO 178 |
| 简支梁缺口冲击强度, +23°C |
21[1] |
kJ/m² |
ISO 179/1eA |
| 简支梁缺口冲击强度, -30°C |
11[1] |
kJ/m² |
ISO 179/1eA |
| 悬臂梁缺口冲击强度, +23°C |
20[1] |
kJ/m² |
ISO 180/1A |
| 悬臂梁缺口冲击强度 |
11[1] |
kJ/m² |
ISO 180/1A |
| 悬臂梁缺口冲击强度 - 温度 |
-40 |
°C |
- |
| 洛克硬度 |
R 114 |
- |
ISO 2039-2 |
| ASTM数据 |
| 拉伸模量 |
2630 |
MPa |
ASTM D 638 |
| 屈服应力 |
59.8 |
MPa |
ASTM D 638 |
| 断裂拉伸强度 |
50 |
MPa |
ASTM D 638 |
| 屈服伸长率 |
4 |
% |
ASTM D 638 |
| 断裂伸长率 |
80 |
% |
ASTM D 638 |
| 弯曲模量 |
2501 |
MPa |
ASTM D 790 |
| 弯曲强度 |
99.1 |
MPa |
ASTM D 790 |
| 洛克硬度 |
R 114 |
- |
ASTM D 785 |
| 悬臂梁缺口冲击强度, 1/8 in |
598 |
J/m |
ASTM D 256 |
| 悬臂梁缺口冲击强度, 1/4 in |
157 |
J/m |
ASTM D 256 |
| 低温悬臂梁缺口冲击强度, Low-Temperature |
118 |
J/m |
ASTM D 256 |
| 温度 |
-30 |
°C |
- |
| 热性能 | 价值 | 单位 | Test Standard |
| ISO数据 |
| 热变形温度, 1.80 MPa |
84 |
°C |
ISO 75-1/-2 |
| 热变形温度, 0.45 MPa |
92 |
°C |
ISO 75-1/-2 |
| 维卡软化温度, B |
101 |
°C |
ISO 306 |
| 线性热膨胀系数, 平行 |
78 |
E-6/K |
ISO 11359-1/-2 |
| 线性热膨胀系数, 垂直 |
88 |
E-6/K |
ISO 11359-1/-2 |
| 厚度为h时的燃烧性 |
V-0 |
class |
IEC 60695-11-10 |
| 测试用试样的厚度 |
1.2 |
mm |
- |
| 厚度为h时的5V燃烧性 |
5VB |
class |
IEC 60695-11-20 |
| 测试用试样的厚度 |
1.5 |
mm |
- |
| ASTM数据 |
| UL94 燃烧性 |
V-2 |
- |
UL 94 |
| 测试厚度 |
0.8 |
mm |
- |
| 热释放速率, 平行 |
78 |
E-6/K |
ASTM D 696 |
| 热释放速率, 垂直 |
88 |
E-6/K |
ASTM D 696 |
| DTUL @ 66 psi |
95[2] |
°C |
ASTM D 648 |
| DTUL @ 264 psi |
86[2] |
°C |
ASTM D 648 |
| 维卡温度 |
101 |
°C |
ASTM D 1525 |
| 电性能 | 价值 | 单位 | Test Standard |
| ISO数据 |
| 体积电阻率 |
1E15 |
Ohm*m |
IEC 62631-3-1 |
| 表面电阻率 |
1E15 |
Ohm |
IEC 62631-3-2 |
| 相对漏电起痕指数 |
325 |
- |
IEC 60112 |
| ASTM数据 |
| 电介质强度, 短时 |
20 |
kV/mm |
ASTM D 149 |
| 表面电阻率 |
1E15 |
Ohm |
ASTM D 257 |
| 体积电阻率 |
1E17 |
Ohm*cm |
ASTM D 257 |
| 其它性能 | 价值 | 单位 | Test Standard |
| 吸湿性 |
0.2 |
% |
类似ISO 62 |
| 密度 |
1190 |
kg/m³ |
ISO 1183 |
| 密度 |
1190 |
kg/m³ |
ASTM D 792 |
| 加工推荐（注塑） | 价值 | 单位 | Test Standard |
| 预干燥-温度 |
75 - 85 |
°C |
- |
| 预干燥-时间 |
3 - 5 |
h |
- |
| 加工湿度 |
≤0.02 |
% |
- |
| 注塑熔体温度 |
235 - 265 |
°C |
- |
| 模具温度 |
50 - 80 |
°C |
- |
| 1区 |
220 - 240 |
°C |
- |
| 2区 |
235 - 255 |
°C |
- |
| 3区 |
250 - 265 |
°C |
- |
| 喷嘴温度 |
250 - 265 |
°C |
- |
典型数据
加工方法
注塑
特殊性能
阻燃的, 无卤
应用
汽车, 电子电气, 通用
地区供应
北美, 欧洲, 亚太, 中南美洲
权利义务的法律声明
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com
Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.
Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.