Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of Pebax® MV 1074 SP 01 - TPA - ARKEMA

Check here, which other Pebax datasheets, application examples or technical articles are available in Material Data Center

机械性能 - 热性能 - 电性能 - 其它性能 - 机械性能(薄膜) - 函数

Any use of this information falls under the rules of our disclaimer.

材料文字说明

Polyether block amide Pebax® MV 1074 SP 01 resin is a thermoplastic elastomer made of flexible polyether and rigid polyamide.
Pebax® MV 1074 SP 01 resin is an inherently dissipative polymer and can be dry blended or compounded with an isolative polymer to lower the surface resistivity. This hydrophilic grade when extruded into either a thin film or laminated on to a substrate offers excellent permeability to moisture vapor while remaining waterproof.
This SP grade has been developed to be heat and UV resistant.

Refractive index according to an internal method is 1.502.


Main applications:

• Breathable membranes
• Permanent antistactic additive

Packaging:
This grade is delivered dried in sealed packaging (25 kg bags) ready to be processed.

Shelf Life:
Two years from the delivery. For any use above this limit, please refer to our technical services.

机械性能	干 / 已调节	单位	Test Standard
ISO数据
拉伸模量	97 / 80	MPa	ISO 527
50％伸长率时的应力S	10 / 10	MPa	ISO 527
断裂伸长率	>50 / >50	%	ISO 527
断裂应力 TPE	30 / *	MPa	ISO 527
断裂应变 TPE	>300 / *	%	ISO 527
肖氏硬度D	38 / *	-	ISO 7619-1

热性能	干 / 已调节	单位	Test Standard
ISO数据
熔融温度, 10°C/min	158 / *	°C	ISO 11357-1/-3
玻璃化转变温度, 10°C/min	-40 / *	°C	ISO 11357-1/-2
燃烧性－氧指数	19 / *	%	ISO 4589-1/-2

电性能	干 / 已调节	单位	Test Standard
ISO数据
体积电阻率	1.5E9 / 2.5E7	Ohm*m	IEC 62631-3-1
表面电阻率	* / 3E9	Ohm	IEC 62631-3-2
介电强度	5 / -	kV/mm	IEC 60243-1

其它性能	干 / 已调节	单位	Test Standard
吸水性	48 / *	%	类似ISO 62
吸湿性	1.4 / *	%	类似ISO 62
密度	1070 / -	kg/m³	ISO 1183

机械性能(薄膜)	干 / 已调节	单位	Test Standard
ISO数据
最大应力, 平行	32 / *	MPa	ISO 527-3
最大应力, 垂直	34 / *	MPa	ISO 527-3
最大应变, 平行	500 / *	%	ISO 527-3
最大应变, 垂直	700 / *	%	ISO 527-3

函数

典型数据

加工方法

注塑, 薄膜挤出成型, 异型材挤出成型, 其它挤出成型, 模压/烧结成型, 浇铸成型, 热成型

供货形式

粒料

特殊性能

提高导电性, 防静电的, 经光稳处理的/耐光的, 经耐紫外线处理的/耐气候的, 经热稳处理的/耐热的

地区供应

北美, 欧洲, 亚太, 中南美洲, 中东/非洲

其他信息

注塑成型

Processing conditions:

- Typical melt temperature (Min / Recommended / Max): 200°C / 240°C / 270°C.
- Typical mold temperature: 25–60°C.
- Drying time and temperature (only necessary for bags opened for more than two hours): 4-6 hours at 65-75°C.

其E烦龀尚

Processing conditions:

- Typical melt temperature (Min / Recommended / Max): 210°C / 220°C / 230°C.
- Drying time and temperature (only necessary for bags opened for more than two hours): 4-6 hours at 65-75°C.

耐化学性

酸类
	硫酸 (38g/100g) (23°C)
碱类
	氢氧化钠溶液 (1g/100g) (23°C)
碳氢化合物
	异辛烷 (23°C)
酮类
	丙酮 (23°C)
盐溶液
	氯化锌溶液 (50g/100g) (23°C)
其它
	水 (23°C)

权利义务的法律声明

Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.

Created: Source: www.materialdatacenter.com