Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of RAVAMID® R200 T51 - PA6 - Ravago Group

Material Data Center offers the following functions for RAVAMID® R200 T51:
unit conversion, PDF datasheet print, comparison with other plastics

Check here, which other Ravamid datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
加工/物理特性 - 机械性能 - 热性能 - 电性能 - 其它性能 - 加工推荐（注塑）
Any use of this information falls under the rules of our disclaimer.
加工/物理特性价值单位Test Standard
ISO数据
熔融指数, MFI 22 g/10min ISO 1133
温度 250 °C -
负载 2.16 kg -
模塑收缩率, 平行 1.1 % ISO 294-4, 2577
机械性能价值单位Test Standard
ISO数据
屈服应力 50 MPa ISO 527
断裂应力 40 MPa ISO 527
断裂伸长率 40 % ISO 527
弯曲模量, 23°C 1800 MPa ISO 178
弯曲强度 45 MPa ISO 178
简支梁缺口冲击强度, +23°C 14 kJ/m² ISO 179/1eA
Izod冲击强度, +23°C N kJ/m² ISO 180/1U
悬臂梁缺口冲击强度, +23°C 16 kJ/m² ISO 180/1A
悬臂梁缺口冲击强度 10 kJ/m² ISO 180/1A
悬臂梁缺口冲击强度 - 温度 -30 °C -
热性能价值单位Test Standard
ISO数据
熔融温度, 10°C/min 220 °C ISO 11357-1/-3
热变形温度, 1.80 MPa 55 °C ISO 75-1/-2
维卡软化温度, B 180 °C ISO 306
1.5mm名义厚度时的燃烧性 HB class IEC 60695-11-10
测试用试样的厚度 1.6 mm -
厚度为h时的燃烧性 HB class IEC 60695-11-10
测试用试样的厚度 0.8 mm -
燃烧速率, FMVSS, 厚度：1毫米 34 mm/min ISO 3795 (FMVSS 302)
灼热丝燃烧指数 (GWFI) 650 °C IEC 60695-2-12
GWFI - 测试用试样厚度 2 mm -
电性能价值单位Test Standard
ISO数据
介电强度 18 kV/mm IEC 60243-1
相对漏电起痕指数 600 - IEC 60112
其它性能价值单位Test Standard
吸湿性 1.5 % 类似ISO 62
密度 1090 kg/m³ ISO 1183
加工推荐（注塑）价值单位Test Standard
预干燥-温度 75 °C -
预干燥-时间 3 - 4 h -
加工湿度 ≤0.12 % -
注塑熔体温度 240 - 270 °C -
模具温度 70 - 90 °C -
1区 220 - 230 °C -
2区 230 - 245 °C -
3区 250 - 260 °C -
喷嘴温度 250 - 260 °C -
螺杆转速 50 - 80 rpm -
背压 0.4 - 0.8 MPa -
保压压力 6 - 8 MPa -
典型数据
特殊性能
高冲击韧性的/经抗冲改性的, 经耐紫外线处理的/耐气候的, 经热稳处理的/耐热的
地区供应
欧洲
权利义务的法律声明
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com