Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of VANDAR® 4602Z - PBT - Celanese

Material Data Center offers the following functions for VANDAR® 4602Z:
unit conversion, PDF datasheet print, comparison with other plastics, snap fit calculation, beam deflection calculation, CAE Interfaces

Check here, which other Vandar datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Any use of this information falls under the rules of our disclaimer.
材料文字说明
4602Z is an unfilled thermoplastic alloy with good weatherability and chemical resistance.

Flammability at thickness h (0.85 mm)HB-
加工/物理特性价值单位Test Standard
ISO数据
熔体体积流动速度, MVR 9 cm³/10min ISO 1133
温度 250 °C -
载荷 5 kg -
模塑收缩率, 平行 1.9 % ISO 294-4, 2577
模塑收缩率, 垂直 1.9 % ISO 294-4, 2577
机械性能价值单位Test Standard
ISO数据
拉伸模量 1400 MPa ISO 527
屈服应力 31 MPa ISO 527
屈服伸长率 5.5 % ISO 527
名义断裂伸长率 >50 % ISO 527
无缺口简支梁冲击强度, +23°C N kJ/m² ISO 179/1eU
简支梁冲击强度, -30°C N kJ/m² ISO 179/1eU
简支梁缺口冲击强度, +23°C 70 kJ/m² ISO 179/1eA
简支梁缺口冲击强度, -30°C 10 kJ/m² ISO 179/1eA
热性能价值单位Test Standard
ISO数据
熔融温度, 10°C/min 225 °C ISO 11357-1/-3
玻璃化转变温度, 10°C/min 60 °C ISO 11357-1/-2
热变形温度, 1.80 MPa 48 °C ISO 75-1/-2
热变形温度, 0.45 MPa 110 °C ISO 75-1/-2
维卡软化温度, B 130 °C ISO 306
线性热膨胀系数, 平行 120 E-6/K ISO 11359-1/-2
线性热膨胀系数, 垂直 114 E-6/K ISO 11359-1/-2
厚度为h时的燃烧性 HB class IEC 60695-11-10
测试用试样的厚度 0.8 mm -
电性能价值单位Test Standard
ISO数据
相对介电常数., 100Hz 4.4 - IEC 62631-2-1
相对介电常数., 1MHz 3.9 - IEC 62631-2-1
介质损耗因子, 100Hz 75 E-4 IEC 62631-2-1
介质损耗因子, 1MHz 310 E-4 IEC 62631-2-1
体积电阻率 1E12 Ohm*m IEC 62631-3-1
表面电阻率 1E14 Ohm IEC 62631-3-2
介电强度 24 kV/mm IEC 60243-1
其它性能价值单位Test Standard
吸水性 0.45 % 类似ISO 62
吸湿性 0.2 % 类似ISO 62
密度 1250 kg/m³ ISO 1183
函数
动态剪切模量-温度 , VANDAR® 4602Z, PBT, Celanese
应力-应变.  , VANDAR® 4602Z, PBT, Celanese
正割模量-应变.  , VANDAR® 4602Z, PBT, Celanese
典型数据
加工方法
注塑
供货形式
粒料
添加剂
润滑剂
特殊性能
经耐紫外线处理的/耐气候的, 经热稳处理的/耐热的
耐化学试剂
通用耐化学性
地区供应
北美, 欧洲, 亚太, 中南美洲, 中东/非洲
其他信息
注塑成型
To avoid hydrolytic degradation during processing, Vandar resins have to be dried to a moisture level equal to or less than 0.02%. Drying should be done in a dehumidifying hopper dryer capable of dewpoints <-30°F (-34°C) at 250°F (121°C) for 4 hours.
Rear Temperature 450-480(230-250) deg F (deg C)
Center Temperature 460-490(235-255) deg F (deg C)
Front Temperature 470-500(240-260) deg F (deg C)
Nozzle Temperature 470-510(240-265) deg F (deg C)
Melt Temperature 470-510(240-265) deg F (deg C)
Mold Temperature 100-200(40-95 deg F (deg C)
Back Pressure 0-50 psi
Screw Speed Moderate
Injection Speed Fast

Injection speed, injection pressure and holding pressure have to be optimized to the individual article geometry. To avoid material degradation during processing low back pressure and minimum screw speed have to be used. Overheating of the material has to be avoided, in particular for flame retardant grades. Up to 25% clean and dry regrind may be used.
权利义务的法律声明
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com


Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.

Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.