Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of FORTRON® 4184L6 DW - PPS-(MD+GF)53 - Celanese

Check here, which other Fortron datasheets, application examples or technical articles are available in Material Data Center

加工/物理特性 - 机械性能 - 热性能 - 电性能 - 其它性能 - 函数

Any use of this information falls under the rules of our disclaimer.

材料文字说明

Fortron 4184L6 is an easier flow version of Fortron 4184L4. for drinking water applications.  It offers similar characteristics to the 4184L4. This grade is especially used for thin walled parts requiring long flow lengths, stiffness and dimensional control. Applications made of this grade are typically electronic components.

Flammability @1.6mm nom. thickn.	V-0	-
Flammability at thickness h (0.75 mm)	V-0	-

加工/物理特性	价值	单位	Test Standard
ISO数据
模塑收缩率, 平行	0.3	%	ISO 294-4, 2577
模塑收缩率, 垂直	0.6	%	ISO 294-4, 2577
熔体的比热	1500	J/(kg K)	-

机械性能	价值	单位	Test Standard
ISO数据
拉伸模量	16600	MPa	ISO 527
断裂应力	165	MPa	ISO 527
断裂伸长率	1.4	%	ISO 527
无缺口简支梁冲击强度, +23°C	29	kJ/m²	ISO 179/1eU
简支梁冲击强度, -30°C	29	kJ/m²	ISO 179/1eU
简支梁缺口冲击强度, +23°C	7	kJ/m²	ISO 179/1eA
简支梁缺口冲击强度, -30°C	7	kJ/m²	ISO 179/1eA

热性能	价值	单位	Test Standard
ISO数据
熔融温度, 10°C/min	280	°C	ISO 11357-1/-3
玻璃化转变温度, 10°C/min	90	°C	ISO 11357-1/-2
热变形温度, 1.80 MPa	270	°C	ISO 75-1/-2
热变形温度, 8.00 MPa	215	°C	ISO 75-1/-2
线性热膨胀系数, 平行	24	E-6/K	ISO 11359-1/-2
线性热膨胀系数, 垂直	32	E-6/K	ISO 11359-1/-2
1.5mm名义厚度时的燃烧性	V-0	class	IEC 60695-11-10
测试用试样的厚度	1.5	mm	-
厚度为h时的燃烧性	V-0	class	IEC 60695-11-10
测试用试样的厚度	0.8	mm	-

电性能	价值	单位	Test Standard
ISO数据
相对介电常数., 1MHz	4.7	-	IEC 62631-2-1
介质损耗因子, 1MHz	20	E-4	IEC 62631-2-1
体积电阻率	>1E13	Ohm*m	IEC 62631-3-1
表面电阻率	>1E15	Ohm	IEC 62631-3-2
介电强度	27	kV/mm	IEC 60243-1

其它性能	价值	单位	Test Standard
吸水性	0.02	%	类似ISO 62
密度	1800	kg/m³	ISO 1183

函数

典型数据

加工方法

注塑

供货形式

粒料

添加剂

脱模助剂

特殊性能

经光稳处理的/耐光的, 经热稳处理的/耐热的

其他信息

注塑成型

Predrying in a dehumidified air dryer at 130 - 140 degC/3-4 hours is recommended.
On injection molding machines with 15-25 D long three-section screws, as are usual in the trade, the FORTRON is processable. A shut-off nozzle is preferred to a free-flow nozzle.

Melt temperature 320-340 degC
Mold wall temperature at least 140 degC

A medium injection rate is normally preferred. All mold cavities must be effectively vented.
Tool temperature of at least 135 degC is recommended for parts to achieve maximum crystallizable potential.

权利义务的法律声明

Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.

Created: Source: www.materialdatacenter.com