Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of Pebax® 7233 SP 01 - TPA - ARKEMA

Check here, which other Pebax datasheets, application examples or technical articles are available in Material Data Center

加工/物理特性 - 机械性能 - 热性能 - 电性能 - 其它性能 - 函数

Any use of this information falls under the rules of our disclaimer.

材料文字说明

Polyether block amide Pebax® 7233 SP 01 resin is a thermoplastic elastomer made of flexible polyether and rigid polyamide.
This SP grade has been developed to be heat and UV resistant.


Main applications:

• Athletic foot wear components
• Ski shoes
• Zip fasteners
• Hook and loop fasteners

Packaging:
This grade is delivered dried in sealed packaging (20 or 25 kg bags) ready to be processed.

Shelf Life:
Two years from the delivery. For any use above this limit, please refer to our technical services.

加工/物理特性	干 / 已调节	单位	Test Standard
ISO数据
模塑收缩率, 平行	1.1 / *	%	ISO 294-4, 2577
模塑收缩率, 垂直	1.3 / *	%	ISO 294-4, 2577

机械性能	干 / 已调节	单位	Test Standard
ISO数据
拉伸模量	- / 510	MPa	ISO 527
屈服应力	- / 26	MPa	ISO 527
屈服伸长率	- / 18	%	ISO 527
名义断裂伸长率	- / >50	%	ISO 527
简支梁缺口冲击强度, +23°C	- / 15	kJ/m²	ISO 179/1eA
简支梁缺口冲击强度, -30°C	- / 10	kJ/m²	ISO 179/1eA
10%应变时的应力	29 / *	MPa	ISO 527
100%应变时的应力	25 / *	MPa	ISO 527
断裂应力 TPE	56 / *	MPa	ISO 527
断裂应变 TPE	>300 / *	%	ISO 527
撕裂强度	166 / *	kN/m	ISO 34-1
肖氏硬度D	61 / *	-	ISO 7619-1

热性能	干 / 已调节	单位	Test Standard
ISO数据
熔融温度, 10°C/min	174 / *	°C	ISO 11357-1/-3
维卡软化温度, B	106 / *	°C	ISO 306
线性热膨胀系数, 平行	120 / *	E-6/K	ISO 11359-1/-2

电性能	干 / 已调节	单位	Test Standard
ISO数据
相对介电常数., 100Hz	7 / -	-	IEC 62631-2-1
相对介电常数., 1MHz	4 / -	-	IEC 62631-2-1
介质损耗因子, 100Hz	1630 / -	E-4	IEC 62631-2-1
介质损耗因子, 1MHz	586 / -	E-4	IEC 62631-2-1
体积电阻率	8E11 / -	Ohm*m	IEC 62631-3-1
表面电阻率	* / 1.84E14	Ohm	IEC 62631-3-2
介电强度	44.5 / -	kV/mm	IEC 60243-1
相对漏电起痕指数	* / 600	-	IEC 60112

其它性能	干 / 已调节	单位	Test Standard
吸水性	0.9 / *	%	类似ISO 62
吸湿性	0.7 / *	%	类似ISO 62
密度	1010 / 1010	kg/m³	ISO 1183

函数

典型数据

加工方法

注塑, 薄膜挤出成型, 异型材挤出成型, 其它挤出成型, 模压/烧结成型, 浇铸成型, 热成型

供货形式

粒料

特殊性能

可电镀的, 经光稳处理的/耐光的, 经耐紫外线处理的/耐气候的, 经热稳处理的/耐热的

地区供应

北美, 欧洲, 亚太, 中南美洲, 中东/非洲

其他信息

注塑成型

Processing conditions:

- Typical melt temperature (Min / Recommended / Max) : 230°C / 260°C / 290°C.
- Typical mold temperature : 25 – 60°C.
- Drying time and temperature (only necessary for bags opened for more than two hours) : 5-7 hours at 70-80°C.

其E烦龀尚

Processing conditions:

- Typical melt temperature (Min / Recommended / Max) : 220°C / 235°C / 250°C.
- Drying time and temperature (only necessary for bags opened for more than two hours) : 5-7 hours at 70-80°C.

耐化学性

酸类
	硫酸 (38g/100g) (23°C)
碱类
	氢氧化钠溶液 (1g/100g) (23°C)
醇类
	乙醇 (23°C)
碳氢化合物
	异辛烷 (23°C)
酮类
	丙酮 (23°C)
盐溶液
	氯化锌溶液 (50g/100g) (23°C)
其它
	水 (23°C)

权利义务的法律声明

Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.

Created: Source: www.materialdatacenter.com

Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.

Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.